PVD processes require different materials to be coated separately. It is essential to identify and distinguish the various types of substrate before putting them into production.
The thickness of the decorative coatings is in the order of a few tenths of a micron, from 0.3 to 0.7µm. Therefore, given the traditional tolerances for PVD-coated elements in the taps and fittings sector, there should be no problems with assembly.
With our technology you can coat all materials as long as they are conductive, keeping in mind certain types that need some considerations. Some metals must be prepared before with a galvanic finish before PVD coating.
Inert, biocompatible PVD coatings can help improve the look and performance of medical devices such as drills, needles and wear parts used in various device assemblies. Photo Credits: Surface Solutions
Physical vapor deposition (PVD) is a vacuum coating process commonly used to improve the performance of cutting tools. Mike Schultz, co-founder of Surface Solutions, says the cathodic-arc PVD coating services his Fridley, Minnesota, company offers can increase the life of a tool as much as 10 times compared to an uncoated tool by providing a harder, more lubricious and wear-resistant surface.
In addition, he says PVD coatings are being increasingly used by medical device manufacturers to differentiate the appearance of their devices from similar products and/or enhance their devices performance, being that the hard, inert coatings are biocompatible and dont react with bone, tissue or bodily fluids. Examples of medical devices the company coats include distractors, drills and needles, but also wear parts used in various device assemblies as well as dental applications.
Schultz says PVD coatings offer improved edge retention so coated surgical instruments remain sharp. For other devices, they can reduce galling between mating stainless steel components, and help prevent oxidation and corrosion.
Here, he answers a few frequently asked questions about PVD coatings:
Cathodic-arc PVD is a process in which various metals are evaporated from a solid source material inside a vacuum chamber using an arc welder. The metals evaporated (such as titanium, chromium, zirconium, aluminum and various other alloys) are reacted with a gas (usually nitrogen and/or a carbon-containing gas) to form a coating material that condenses on the parts to be coated.
Cathodic-arc PVD produces high levels of metal ionization (more than 95% ), which helps ensure high coating adhesion to the substrate material. The process typically has wide operating windows, making it possible to deposit quality coatings using a variety of process parameters. Other coating processes, such as sputtering or ion plating, are not as robust and have smaller operating windows, making it more difficult for them to consistently produce a quality coating.
To achieve a well-adhered coating, it is very important that the parts to be coated are clean. Part surfaces must be free of oxides, EDM recast and organic films, because such contaminants can adversely affect coating quality.
Effective masking ensures the PVD coating is applied only where it is required.
To remove contaminants before coating, coating companies use techniques such as polishing, tumbling, acid etching, and sand and glass-bead blasting. Some of these techniques can alter the surface finish of the part being coated, however, so the coating company often works with the customer to develop a process that meets the customers expectations for coating quality and part appearance.
If a part has sharp edges, cleaning processes that could adversely affect edge sharpness would not be used. Additionally, if tiny or very fragile parts are being coated, coating process modifications can be made to reduce heat-up and coating rates. These modifications ensure that delicate features are not overheated and the coating is not too thick.
PVD coatings are very thin (typically ranging from 0. to 0. inch) and usually replicate a parts original finish (unless an abrasive cleaning process is used). Best results are attained when part surfaces are smooth. As a result, ground or polished surfaces will often yield better results than bead-blasted or matte surface finishes.
Recommended article:If you want to learn more, please visit our website Blue Hairline Stainless Steel Sheets.
If a matte finish on a specific area of a part is desired, it might be best to allow the coater to produce the texture on the part. Texturing by the part supplier could produce contamination on that area of the part, which would require some rework, negating any savings the supplier was perhaps counting on attaining.
Typical coating temperature for all Surface Solutions PVD coatings is approximately 800°F. Coating temperature can alter the hardness of parts or cause them to distort (shrink or grow). To minimize this possible effect, we suggest that heat-sensitive parts be tempered at 900 to 950°F before they are sent to be coated.
PVD coatings can be applied to most metals that can withstand being heated to 800°F. Commonly coated medical materials include 303, 440C and 17-4 stainless steels; titanium alloys; and some tool steels. PVD coatings are typically not applied to aluminum, because the temperature of the coating process is close to the materials melting point.
Surface Solutions offers four PVD coatings for medical devices. The most commonly used is titanium nitride (TiN), which has a thickness ranging from 0. to 0. inch, Vickers hardness ranging from 2,400 to 2,600 Hv, and a gold color.
This multilayer coating has zirconium nitride (ZrN) as the top layer and results in a silver-gold color and offers high hardness.
The second most common medical coating is aluminum titanium nitride (AlTiN), often referred to as the black nitride or black titanium coating. It has a thickness ranging from 0. to 0. inch, hardness ranging from 4,000 to 4,200 Hv, and a charcoal black finish.
Two other medical coatings the company offers are chrome nitride (CrN) and Alpha. CrN has a thickness ranging from 0. to 0. inch, hardness ranging from 2,200 to 2,400 Hv, and a silver finish. Alpha is a multilayer coating that has zirconium nitride (ZrN) as the top layer and results in a silver-gold color. It has thickness ranging from 0. to 0. inch and offers the highest hardness, ranging from 4,400 to 4,600 Hv. The company says this coating can last two to four times longer than TiN due to its higher hardness, lubricity and abrasion resistance.
Compared to a chemical vapor deposition process (CVD), PVD coatings are applied at a much lower temperature, and PVD-coated parts dont have to be heat treated again after coating. Also, PVD replicates the surface finish originally on the part, whereas CVD coating results in a matte finish, unless the part is polished after coating.
Surface Solutions coats titanium alloys and believes PVD is more wear-resistant than anodizing and retains its color better over time.
PVD coatings are also commonly used for cutting tools and are said to increase tool life as much as 10 times compared to uncoated tools.
In addition to medical devices and cutting tools, PVD coatings are also commonly used to boost the performance and longevity of punching tools, forming tools and injection-molded wear components. Schultz says medical manufacturers considering PVD coating should discuss their projects with the coating company to ensure they get a functional coating on components where it is needed/desired with the best look possible.
Contact us to discuss your requirements of Etched Stainless Steel Sheet. Our experienced sales team can help you identify the options that best suit your needs.